Single Sided Hard White PVC Foam Tape with Acrylic Adhesive.
Part number: PS082
Single Sided Hard White Class 'O' Fire Retardant PVC Foam Tape with Acrylic Adhesive.
Product Details
Product information
PS082 is primarily a foam compression sealant. The product is a hard grey foam and predominantly closed celled. An acrylic pressure sensitive adhesive is coated on one side, and the product has a paper release liner on the other non-adhesive face. PS080 will act as a water-seal and air/dust seal when compressed.
Its applications include:-
- Compression water seal.
- Preventing electrolytic corrosion.
- Heavy duty applications
- Cushioning.
- Compression air / dust seal.
- Gap filling.
Typical Markets:-
- Construction
- Glazing
- Industrial assembly
- Roofing & Cladding
- Transportation
Accreditations:-
- Fire rated to BS476: Part 6 : 1989 +A1: 2009 and to BS476: Part 7 : 1997 Class 1.
- Complies with the requirements for Class 0 to the Building Regulations 2000.
- Conforms to European Directive 2000/53 EC (lead, chromium VI, mercury, cadmium free)
Features and Benefits
- Minimum 30% compression required to affect a water seal.
- Service temperature –30°C to +70°C Application temperature: +10°C to + 40°C
- Coated on one side with a high-quality pressure sensitive acrylic adhesive.
- Good resistance to dilute acids & alkalis.
- Paper release liner on the non-adhesive face, reducing dimensional change during application.
- Very good Ultra violet {UV} Light resistant
- Resistance to abrasion, corrosion and moisture.
- Suitable for indoor and outdoor environments.
- No known hazards associated with this product.
- Pre-determined dimensional sealant reduces waste.
- Clean to use.
- Colour: White
- Adhesive: Acrylic
- Carrier: PVC Foam
- Thickness: 3.0, 4.5mm
- Foam Density: 240 Kg/m3
- Tensile Strength: 85 Ncm2 (F17)
- Force to Compress By 30%: 5.1 Ncm2 (F4)
- Shore Hardness {OO} Scale: 45“00” (F16)
- Compression Deflection After 1 Minute : 5.1 Ncm-2 (F4)
- 10 Minute 180° Peel Adhesion: 5 N/25mm (F9)
- Elongation at Break: >200% (F17)
- Thermal Conductivity (k): 0.052 Wm1K1